Just like the innovation brought by computer-aided design and manufacturing, our advanced materials for models and molds can provide customers with relevant materials and complete solutions for aircraft design, prototyping, and tooling molds in the aviation field.



Model wood -302- density 0.3, hardness D30-45; Tg-85℃;  1500*500*50/75/100/150/200mm

502- Density 0.47, hardness D50-55; Tg-85℃; 1500*500*50/75/100/150/200mm

700- density 0.72, hardness D65-72; Tg-85℃; 1500*500*20/50/75/100/150/200mm

Pasty substitute wood - SW450- reddish brown; Pasty texture; Operation time 120min; After curing, the density is 0.5 and the hardness is D55;

SW360- orange red; Pasty texture; Operation time is 30-40 minutes; After curing, the density is 0.6 and the hardness is D60-70;

SW325- reddish brown; Pasty texture; Operation time is 30-40 minutes; After curing, the density is 0.7 and the hardness is D65-75;

SW395- earthy red, paste like; Operation time 40-60 minutes; After curing, the density is 0.9 and the hardness is D70-75; Temperature resistance of 140-150 ℃



Application of tooling molds

Block substitute wood - JRJ1600- beige and grey; Density 1.6, Shore D85-90 hardness; 750*500*50/75/100/150mm

Casting resin - EC550- epoxy system; Beige, mixed viscosity 3000mPas; Operation time of 60 minutes; Curing hardness D85;

MC30/ISO1- unfilled PU casting system; Beige, mixed with filler, viscosity 6000mPas; Operation time 40-60 minutes; Curing hardness Shore D85;

Environmentally friendly and odorless, with extremely low heat generation, and a maximum casting thickness of up to 200mm per time;

MC27/ISO4- filled PU casting system, beige, mixed viscosity 3500mPas, operating time 60-70min, curing hardness Shore D85;

Environmentally friendly and odorless, with extremely low heat generation, and a maximum casting thickness of up to 500mm per time;



Application of Composite Material Forming

Mold resin - EC715- aluminum filled hand pasted epoxy system, adjustable operating time (30-100min); Temperature resistance 110-120 ℃

EC138- Hand pasted epoxy mold resin, operation time 70-80min; Temperature resistance up to 150 ℃

EC257- Low viscosity import mold resin, operation time 100-120 minutes; Temperature resistance up to 190-200 ℃



PRA794 and PRA30 flame retardant cast PU resin - used for prototype design and small batch production, certified FAR25 material by the Federal Aviation Administration of the United States.   

Self exhaust vacuum casting resin PRA794 (UL 94 V0);   PRA730  (FAR 25)



Water soluble core resin is used for the production of hollow composite components:

RLF - Water soluble core resin series, resin+filler heat curing, temperature resistance up to 200 ℃ or higher; Commonly used for medium to large composite components.

CAF - Water soluble composite salt mold core series, composite salt formula, temperature resistance of 150-200 ℃; Commonly used for small and medium-sized precision hollow composite components.